Title Reliability based design methodology incorporating residual strength prediction of structural fiber reinforced polymer composites under stochastic variable amplitude fatigue loading
Degree PhD
Department Engineering Science and Mechanics
Advisory Committee
Advisor Name Title
Case, Scott W. Committee Co-Chair
Lesko, John J. Committee Co-Chair
Hyer, Michael W. Committee Member
Riffle, Judy S. Committee Member
Thangjitham, Surot Committee Member
  • Random Loading
  • Probability of failure
  • FRP
  • LRFD
  • Spectrum
Date of Defense 2008-03-18
Availability unrestricted
The research presented in this dissertation furthers the state of the art for reliability-based design of composite structures subjected to high cycle variable amplitude (spectrum) fatigue loads. The focus is on fatigue analyses for axially loaded fiber reinforced polymer (FRP) composites that contain a significant proportion of fibers in the loading direction and thus have fiber-direction dominated failure. The four papers presented in this dissertation describe the logical progression used to develop an improved reliability-based methodology for fatigue-critical design. Throughout the analysis extensive experimental fatigue data on several material systems was used to verify the assumptions and suggest the path forward.

A comparison of 12 fatigue model approaches from the literature showed that a simple linear residual strength approach (Broutman and Sahu) provides an improvement in fatigue life prediction compared to the Palmgren-Miner rule, while more complex residual strength models did not consistently improve on Broutman and Sahu. Evaluation of the effect of load history randomness on fatigue life was made using experimental results for spectra in terms of the first order autocorrelation of the stress events. For approximately reversed Rayleigh distributed fatigue loading, load sequence was not critical in the material behavior. Based on observations of empirical data and evaluation of the micro-mechanics deterioration and failure phenomena of FRP composites under fatigue loading, a new residual strength model for the tension and compression under any load history was proposed. Then this model was implemented in a stochastic framework and a method was proposed to enable calculation of the load and resistance factor design (LRFD) parameters for realistic reliabilities with relatively few computations. The proposed approach has significant advantages over traditional lifetime-damage-sum-based reliability analysis and provides a significant step toward enabling more accurate reliability-based design with composite materials.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  AppendixB_POST2007R_def.txt 14.73 Mb 01:08:12 00:35:04 00:30:41 00:15:20 00:01:18
  AppendixB_VT8084DataSet.xls 2.28 Mb 00:10:34 00:05:26 00:04:45 00:02:22 00:00:12
  POST_N_L_Dissertation_2008_2.pdf 3.83 Mb 00:17:44 00:09:07 00:07:59 00:03:59 00:00:20

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.