Title page for ETD etd-07132000-14530012

Type of Document Master's Thesis
Author Senne, Jolyn Louise
Author's Email Address jsenne@vt.edu
URN etd-07132000-14530012
Title Fatigue Life of Hybrid FRP Composite Beams
Degree Master of Science
Department Engineering Mechanics
Advisory Committee
Advisor Name Title
Lesko, John Committee Chair
Case, Scott W. Committee Member
Cousins, Thomas E. Committee Member
  • pultruded composites
  • hybrid composites
  • fiber-reinforced polymer (FRP) composites
  • life prediction
  • fatigue
  • infrastructure
Date of Defense 2000-07-10
Availability unrestricted
As fiber reinforced polymer (FRP) structures find application in highway bridge structures, methodologies for describing their long-term performance under service loading will be a necessity for designers. The designer of FRP bridge structures is faced with out-of-plane damage and delamination at ply interfaces. The damage most often occurs between hybrid plys and dominates the life time response of a thick section FRP structure. The focus of this work is on the performance of the 20.3 cm (8 in) pultruded, hybrid double web I-beam structural shape. Experimental four-point bend fatigue results indicate that overall stiffness reduction of the structure is controlled by the degradation of the tensile flange. The loss of stiffness in the tensile flange results in the redistribution of the stresses and strains, until the initiation of failure by delamination in the compression flange. These observations become the basis of the assumptions used to develop an analytical life prediction model. In the model, the tensile flange stiffness is reduced based on coupon test data, and is used to determine the overall strength reduction of the beam in accordance the residual strength life prediction methodology. Delamination initiation is based on the out-of-plane stress sz at the free edge. The stresses are calculated using two different approximations, the Primitive Delamination Model and the Minimization of Complementary Energy. The model successfully describes the onset of delamination prior to fiber failure and suggests that out-of-plane failure controls the life of the structure.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  ms_thesis_jsenne.pdf 1.31 Mb 00:06:03 00:03:06 00:02:43 00:01:21 00:00:06

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.