Title page for ETD etd-09302005-134815

Type of Document Dissertation
Author Uan-Zo-li, Julie Tammy
URN etd-09302005-134815
Title Morphology, Crystallization and Melting Behavior of Propylene-Ethylene Statistical Copolymers
Degree PhD
Department Materials Science and Engineering
Advisory Committee
Advisor Name Title
Marand, Hervé L. Committee Chair
Davis, Richey M. Committee Member
Esker, Alan R. Committee Member
Love, Brian J. Committee Member
Reynolds, William T. Jr. Committee Member
  • alpha and gamma phases
  • ethylene inclusion
  • rigid amorphous fraction
  • thermodynamic heat of fusion
  • propylene-ethylene copolymers
Date of Defense 2005-09-19
Availability unrestricted

In this work the morphology, crystallization and melting behavior of novel Dow Chemical propylene-ethylene copolymers were investigated.

The incorporation of ethylene units into a polypropylene chain resulted in the decrease in crystallization, melting and glass transition temperatures and overall crystallinity. Based on the shape of heat capacity curves and the dependence of the melting temperature offset on ethylene content, it was concluded that copolymers prepared using different catalyst systems exhibited different ethylene sequence length distributions.

The behavior of Dow Chemical propylene-ethylene copolymers was compared to that of copolymers prepared using traditional metallocene and Ziegler-Natta catalysts. The catalyst system used in the preparation of these new copolymers is similar to a metallocene catalyst system.

It was demonstrated that ethylene defects are partially included in the polypropylene crystal. The thermodynamic heat of fusion at the equilibrium melting temperature decreased by 44% with an increase in ethylene concentration from 0 mol% to 21.2 mol%. On the basis of calorimetric and density data, the inclusion model based on the Sanchez-Eby crystallization theory was shown to be applicable for the evaluation of the degree of crystallinity. At the same time, inadequacies were found in application of the rigid amorphous fraction model to these copolymers.

The formation of gamma-phase crystals was shown to be favored by both an increase in the ethylene content and a decrease in the crystallization rate. Increase in the ethylene content was shown to lead to a decrease in the density, length and thickness of alpha-phase crystals. It was also demonstrated that the cross-hatching morphology is present in all propylene-ethylene copolymers.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  Dissertation_final_2.pdf 5.74 Mb 00:26:34 00:13:40 00:11:57 00:05:58 00:00:30

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.