Title A study of contact between a profile meter stylus and polymer films on roughened substrates
Degree Master of Science
Department Mechanical Engineering
Advisory Committee
Advisor Name Title
N. S. Eiss, Jr. Committee Chair
C. E. Knight Committee Member
H. H. Mabie Committee Member
  • Surfaces (Technology)
Date of Defense 1985-12-05
Availability restricted
When a polymer film is deposited onto a roughened substrate, the film masks over the underlying substrate roughness. Then when attempting to

measure the roughness of the polymer film surface using a stylus-type profile meter, the pressure between the tip of the stylus and the film

is sufficient to plastically deform the polymer surface. The result is a possible erroneous measurement of the surface roughness of the polymer film. This thesis reports on attempts to quantify the actual roughness of the polymer film from the measurement obtained by the profile meter. Extensive surface profile data were collected and analyzed to determine the characteristics of the surface of the substrate and of the coating on the substrate. The tracks made by the stylus in the film were then observed in a scanning electron microscope, from which the depth of the stylus tracks were measured. The effects of the film thickness, stylus traversing speed, and substrate roughness on the stylus penetration depth, the variation in the depth, and the measured film roughness are assessed and discussed. It was found that using the fastest stylus traversing speed minimizes the variation of the stylus penetration depth and thus results in the most accurate measurement of the film surface. To predict this stylus indentation depth, a plane strain plastic deformation

model is developed using slip—line field theory. It is found that the slip-line model gives good estimates of the stylus indentation depth

when the film thickness is large.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
[VT] LD5655.V855_1985.G574.pdf 6.57 Mb 00:30:23 00:15:37 00:13:40 00:06:50 00:00:35
[BTD] next to an author's name indicates that all files or directories associated with their ETD are accessible from the Virginia Tech campus network only.

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.