Title page for ETD etd-12142010-150936

Type of Document Master's Thesis
Author Tian, Zhipeng
URN etd-12142010-150936
Title Nanopore/Nanotube Pattern Formation through Focused Ion Beam Guided Anodization
Degree Master of Science
Department Materials Science and Engineering
Advisory Committee
Advisor Name Title
Lu, P. Kathy Committee Chair
Aning, Alexander O. Committee Member
Clark, David E. Committee Member
  • Titania Nanotube
  • Porous Aluminium Oxide
  • Patterning
  • Anodization
  • Focused Ion Beam
Date of Defense 2010-12-01
Availability restricted
Anodization is a kind of method that can produce oxide layer in a large area and on flexible shaped metals. In some specific conditions, anodic oxide layers exhibit interesting nanopore/nanotube structures. In this work, focused ion beam patterning method is introduced to general anodization, aiming to make highly ordered anodic porous alumina and titania nanotubes.

Focused ion beam guided porous anodic alumina is carried out by pre-designing hexagonal and square guiding patterns with different interpore distances on well electropolished Al foil before anodization. After anodization, the guiding interpore distance is found to affect the new pores’ locations and shapes. Two important elements, electrical field and mechanical stress, are discussed for the development of the guiding pores and the generation of new pores. Based on the proposed pore growth mechanism, novel patterns, non-spherical pores, and large patterns across the grain boundaries are successfully produced.

The research on focused ion beam guided anodic titania nanotubes begins with surface polishing. The influence of four polishing conditions, as-received, chemically polished, mechanically polished, and electropolished samples, are investigated. A polished smooth sample provides a desired surface for focused ion beam guided anodization. Hexagonal guiding patterns with different interpore distances are created on Ti surface. Ordered nanotube arrays are produced, and the structure of the anodized guiding pattern is identified.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
[VT] Tian_Z_T_2010.pdf 13.25 Mb 01:01:20 00:31:32 00:27:36 00:13:48 00:01:10
[VT] indicates that a file or directory is accessible from the Virginia Tech campus network only.

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.