Title Modeling the Time-to Corrosion Cracking of the Cover Concrete in Chloride Contaminated Reinforced Concrete Structures
Degree PhD
Department Civil Engineering
Advisory Committee
Advisor Name Title
Al-Qadi, Imadeddin L.
Barker, Richard M.
Brown, Jesse J. Jr.
Walker, Richard D.
Weyers, Richard E. Committee Chair
  • deterioration
  • chloride
  • corrosion
  • cracking
  • model
Date of Defense 1996-10-21
Availability unrestricted
Significant factors on steel corrosion in chloride contaminated reinforced concrete and time-to-corrosion cracking were investigated in this study. Sixty specimens were designed with seven admixed chloride contents, three concrete cover depths, two reinforcing steel bar diameters, two exposure conditions, and a typical concrete with water to cement ratio of 0.45. Corrosion current density (corrosion rate), corrosion potential, ohmic resistance of concrete and temperature were measured monthly on these specimens using both the 3LP and Gecor devices. Metal loss measurements were performed in accordance with ASTM G1-90, method C3.5, after specimens cracked. The actual corrosion weight loss of the steel reinforcing bars was then compared to the result obtained from the corrosion rate measurement devices. An interaction model for characterizing the dynamic corrosion process was developed based on the five-year corrosion database. The model demonstrates that the corrosion rate is a function of chloride content, temperature at reinforcement depth, ohmic resistance of concrete, and corrosion time after initiation. A time-to-corrosion cracking model was suggested based on a corrosion-cracking conceptual model and critical mass of corrosion products. The model predicted times to corrosion cracking are in good agreement with the observed times to corrosion cracking of the cover concrete.

  Filename       Size       Approximate Download Time (Hours:Minutes:Seconds) 
 28.8 Modem   56K Modem   ISDN (64 Kb)   ISDN (128 Kb)   Higher-speed Access 
  etd.pdf 2.34 Mb 00:10:49 00:05:34 00:04:52 00:02:26 00:00:12
  Liu.pdf 2.34 Mb 00:10:49 00:05:34 00:04:52 00:02:26 00:00:12

Browse All Available ETDs by ( Author | Department )

dla home
etds imagebase journals news ereserve special collections
virgnia tech home contact dla university libraries

If you have questions or technical problems, please Contact DLA.