Type of Document Master's Thesis Author Cavadas, Francisco T. URN etd-04102002-103407 Title Self-Assembled Monolayers As Models For Silica Degree Master of Science Department Chemistry Advisory Committee
Advisor Name Title Deck, Paul A. Committee Chair Anderson, Mark R. Committee Co-Chair Hanson, Brian E. Committee Member Keywords
- Sel-Assembled monolayers
Date of Defense 2001-08-15 Availability unrestricted AbstractThe reaction of hydroquinone and 1,12-dibromododecane affords 4-(12-bromo-dodecyloxy)phenol (4, 7% yield). The alkyl bromide (4) was converted to the corresponding thiol with thiourea to afford 4-(12-mercaptododecyloxy)phenol (1) in 52% yield. The reaction of t-butyllithium with 4-bromoanisole followed by reaction with 1-12-dibromododecane affords a mixture of 4-bromoanisole, 1,12-dibromododecane ,and 4-(12-bromododecyl)-anisole (6). Silica gel chromatography resulted in an inseperable mixture of 4-bromoanisole and (6). Reaction of the mixture with BBr3 afforded 4-(12-bromododecyl)phenol (7) in 34% yield. The alkyl bromide (7) was converted to the corresponding thiol with thiourea to afford 4-(12-mercaptododecyl)phenol (2) in 9% yield. Reduction of 16-mercaptohexadecanoic acid with BH3„hTHF afforded 16-mercaptohexadecanol (3) in 53% yield. All new compounds were characterized by 1H NMR, 13C NMR, transmission IR, HRMS, and, where possible, elemental microanalysis.
Self-assembled monolayers (SAMs) on gold were prepared using thiols 1, 2, and 3. SAMs were characterized using reflectance-absorbance infrared spectroscopy (RAIRS). Diagnostic vibrational modes were assigned by comparing RAIRS spectra to normal mode frequencies and intensities calculated using DFT methods at the 6-31G* level using commercial software. Water droplet goiniometry found contact angles of 52o, 53o, and 64o for SAMs prepared from 1, 2, and 3, respectively. SAMs of 1 and 2 were found to be hydrophilic. When SAMs prepared from 1, 2, and 3 were silylated with phenyldimethylchlorosilane, the resulting contact angles were 78o, 74o, and 75o respectively. A significant increase in contact angles for silylated SAMs of 1 and 2 indicated facile silanization of the surface hydroxides. RAIRS spectra were also obtained for the functionalized SAMs. Silylated SAMs prepared from 1, 2, and 3 are currently under investigation as models for silica-immobilized metallocene olefin polymerization catalysts.
Filename Size Approximate Download Time (Hours:Minutes:Seconds)
28.8 Modem 56K Modem ISDN (64 Kb) ISDN (128 Kb) Higher-speed Access Mastersthesis2.pdf 1.00 Mb 00:04:38 00:02:23 00:02:05 00:01:02 00:00:05
If you have questions or technical problems, please Contact DLA.