Type of Document Master's Thesis Author Xi, Yan Author's Email Address email@example.com URN etd-05222005-141806 Title Ozone Decomposition and Acetone Oxidation on Manganese Oxide Catalysts Degree Master of Science Department Chemical Engineering Advisory Committee
Advisor Name Title Oyama, Shigeo Ted Committee Chair Cox, David F. Committee Member Hanson, Brian E. Committee Member Keywords
- Manganese oxide catalysts
- X-ray absorption spectroscopy
Date of Defense 2005-05-11 Availability unrestricted AbstractThis thesis describes the preparation and characterization of manganese oxide catalysts and their application in the oxidation of acetone, a typical volatile organic compound (VOC), and ozone decomposition. This topic is of great value because of environmental concerns of the elimination of the harmful VOCs and ozone. Manganese oxide was chosen because it is a well-known complete oxidation catalyst for VOCs and also an active catalyst for ozone decomposition. Two cases of studies were carried out in this work.
The first study involved the oxidation of acetone using ozone on silica- and alumina-supported manganese oxide catalysts deposited on aluminum oxide foam substrates. The characteristics of the catalysts were determined through various techniques, including x-ray diffraction (XRD), x-ray absorption spectroscopy (XAS), Brunauer-Emmett-Teller (BET) surface area analysis, temperature-programmed reduction (TPR), and oxygen chemisorption. The use of these techniques allowed better understanding of the nature of the catalysts. Activity tests were carried out in the acetone oxidation reaction and it was found that the usage of ozone substantially reduced the oxidation temperature. Steady-state in situ Raman spectroscopy was also carried out to better understand the mechanism of the acetone oxidation reaction using ozone.
The second study involved an investigation of structural and electronic properties of manganese centers of the MnOx/SiO2 and MnOx/Al2O3 catalysts during the ozone decomposition reaction using in situ x-ray absorption spectroscopy (XAS). The number of surface active sites was again determined through TPR and oxygen chemisorption measurements. The performance of the catalysts with different loadings and supports were also compared.
Filename Size Approximate Download Time (Hours:Minutes:Seconds)
28.8 Modem 56K Modem ISDN (64 Kb) ISDN (128 Kb) Higher-speed Access Abstract.pdf 22.13 Kb 00:00:06 00:00:03 00:00:02 00:00:01 < 00:00:01 Acknowledgements.pdf 15.48 Kb 00:00:04 00:00:02 00:00:01 < 00:00:01 < 00:00:01 Chapter1.pdf 92.39 Kb 00:00:25 00:00:13 00:00:11 00:00:05 < 00:00:01 Chapter2_corrected.pdf 525.34 Kb 00:02:25 00:01:15 00:01:05 00:00:32 00:00:02 Chapter3_corrected.pdf 571.50 Kb 00:02:38 00:01:21 00:01:11 00:00:35 00:00:03 Chapter4.pdf 23.34 Kb 00:00:06 00:00:03 00:00:02 00:00:01 < 00:00:01 Table_of_Contents.pdf 53.39 Kb 00:00:14 00:00:07 00:00:06 00:00:03 < 00:00:01 Title_Page_corrected.pdf 14.68 Kb 00:00:04 00:00:02 00:00:01 < 00:00:01 < 00:00:01 Vita.pdf 12.01 Kb 00:00:03 00:00:01 00:00:01 < 00:00:01 < 00:00:01
If you have questions or technical problems, please Contact DLA.