Type of Document Master's Thesis Author Nazem, Negin Author's Email Address email@example.com URN etd-93097-173344 Title Preparation of highly reflective films by supercritical infusion of a silver additive into poly(ether ether ketone) Degree Master of Science Department Chemical Engineering Advisory Committee
Advisor Name Title Taylor, Larry T. Committee Chair Davis, Richey M. Committee Member Marand, Eva Committee Member Keywords
- Poly(ether ether ketone)
- Supercritical fluid
- Supercritical Fluid Infusion
Date of Defense 1997-10-03 Availability unrestricted AbstractPREPARATION OF HIGHLY REFLECTIVE FILMS BY
SUPERCRITICAL INFUSION OF A SILVER ADDITIVE INTO
POLY(ETHER ETHER KETONE)
There has been a great interest in preparing polymeric reflective surfaces in the last few years. The application of supercritical fluid technology in this area is beginning to receive a great deal of attention. Poly ether ether ketone (PEEK) is well known for its excellent thermal, chemical, mechanical and electrical properties. These properties make it ideal for use in aerospace, electrical, fluid handling and coating industries. Supercritical infusion of a silver-containing additive (1,5-cyclooctadiene- 1,1,1,5,5,5-hexafluoroacetylacetonato)silver(I) into a PEEK film was achieved with moderately high density CO2 at various temperatures, pressures, and times.
During the infusion process: 1) polymer sample was exposed to both supercritical CO2 and the additive under pressure for a brief time, 2) depressurization of the system caused the CO2 to rapidly diffuse out of the polymer; while the remaining additive in the polymer desorbed at a much slower rate governed by its diffusivity in the CO2-free polymer. Following this process the infused film was heated for a short time period to thermally reduce the infused metal and to form a reflective surface. In this research the effect of different additive concentrations, infusion conditions (e.g. temperature, pressure, time), and curing conditions (e.g. air flow rate, temperature, time) on the nature of the PEEK surface will be presented.
Filename Size Approximate Download Time (Hours:Minutes:Seconds)
28.8 Modem 56K Modem ISDN (64 Kb) ISDN (128 Kb) Higher-speed Access THNH.PDF 691.90 Kb 00:03:12 00:01:38 00:01:26 00:00:43 00:00:03
If you have questions or technical problems, please Contact DLA.