Communications Project

Document Type:Master's Thesis
Name:Robert Williamson Gray IV
Title:The Effects of Processing Conditions on Thermoplastic Prototypes Reinforced with Thermotropic Liquid Crystalline Polymers
Degree:Master of Science
Department:Chemical Engineering
Committee Chair: Donald G. Baird
Committee\ Members:
Keywords:Polymer, Composite, TLCP, Prototype, FDM
Date of defense:July 30, 1997
Availability:Release the entire work for Virginia Tech access only.
After one year release worldwide only with written permission of the student and the advisory committee chair.


This work is concerned with preliminary studies on developing thermoplastic composite materials suitable for use in fused deposition modeling (FDM). Polypropylene (PP) strands reinforced with continuous thermotropic liquid crystalline polymer (TLCP) fibrils were generated in a novel dual extruder process. Strands were then re-extruded to form short fiber composite monofilaments that were used as feed stock in the FDM 1600 rapid prototyping system. Prototypes containing 40 wt% Vectra A were shown to have tensile properties twice those of parts built using acrylonitrile butadiene styrene copolymer (ABS), a commercially available material used in the FDM 1600 rapid prototyping system. It was also shown that the final mechanical properties of a composite prototype can be tailored to a specific application by adjusting the lay-down pattern, increasing the functionality of the prototype. In order to obtain the maximum tensile properties in these composite prototype, additional studies were performed to determine the effects of thermal and deformation histories on the mechanical properties of monofilaments that were re-extruded from long fiber TLCP reinforced strands. Strands were consolidated uniaxially at temperatures just above the melting point of the matrix in order to determine the effects of thermal history, and an approximate 20% reduction in tensile modulus relative to the modulus of the strands was observed. Monofilaments that could be used as feed stock in FDM were extruded from long fiber TLCP reinforced strands using a capillary rheometer in order to study the effects of capillary diameter, capillary L/D, and apparent shear rate on the tensile properties.

List of Attached Files


At the author's request, all materials (PDF files, images, etc.) associated with this ETD are accessible from the Virginia Tech network only.

The author grants to Virginia Tech or its agents the right to archive and display their thesis or dissertation in whole or in part in the University Libraries in all forms of media, now or hereafter known. The author retains all proprietary rights, such as patent rights. The author also retains the right to use in future works (such as articles or books) all or part of this thesis or dissertation.